韩国三星毛织:聚丁烯对二酸酯(PBT),Infino: VB-5300G,VB-5300GS,玻璃纤维,阻燃;
| Samsung Cheil Industries Infino® VB-5300G PBT, Glass Filled FR | |||
|---|---|---|---|
| Categories: |
Polymer; Thermoplastic; Polyester, TP; Polybutylene Terephthalate (PBT); Polybutylene Terephthalate (PBT), Glass Fiber Filled, Flame Retardant
|
||
| Material Notes: |
Information provided by Samsung Cheil Industries. |
||
| Vendors: | No vendors are listed for this material. Please click here if you are a supplier and would like information on how to add your listing to this material. | ||
|
|||
Printer friendly version
Download as PDF
Download to Excel (requires Excel and Windows)
Export data to your CAD/FEA program| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.63 g/cc | 1.63 g/cc | ASTM D792 |
| Water Absorption |
0.060 % @Temperature 23.0 °C |
0.060 % @Temperature 73.4 °F |
ASTM D570 |
| Linear Mold Shrinkage, Flow |
0.0030 - 0.0090 cm/cm @Thickness 3.20 mm |
0.0030 - 0.0090 in/in @Thickness 0.126 in |
ASTM D955 |
| Melt Flow |
15 g/10 min @Load 2.16 kg, Temperature 250 °C |
15 g/10 min @Load 4.76 lb, Temperature 482 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 120 | 120 | ASTM D785 |
| Tensile Strength, Yield | 127 MPa | 18500 psi | 5 mm/min; ASTM D638 |
| Elongation at Break | 3.0 % | 3.0 % | 5 mm/min; ASTM D638 |
| Flexural Strength | 186 MPa | 27000 psi | 2.8 mm/min; ASTM D638 |
| Flexural Modulus | 8.83 GPa | 1280 ksi | 2.8 mm/min; ASTM D638 |
| Izod Impact, Notched |
0.735 J/cm @Thickness 3.17 mm |
1.38 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) |
210 °C @Thickness 6.40 mm |
410 °F @Thickness 0.252 in |
ASTM D648 |
| Flammability, UL94 |
V-0 @Thickness 0.750 - 3.00 mm |
V-0 @Thickness 0.0295 - 0.118 in |
|