塑料名称(Polymer)
|
PPE
|
厂商名称(Company)
|
Asahi Chemical 旭化成工业
|
商品名称(Trade Name)
|
XYRON
|
规格(Grade)
|
X9830
|
特征(Characteristic)
|
非强化, 抗化学药品性佳
|
加工方法(Process Method)
|
|
物性名称
|
单位
|
测试方法
|
|
填充剂含量
Filler Content
|
%
|
|
|
比重
Specific Gravity
|
g/cm³
|
ASTM D792
|
1.08
|
融点
Melting Point
|
℃
|
|
|
流动指数
MFR,(MI)
|
g/10 min
|
ASTM D1238
|
23.00
|
吸湿率@24h/23℃
Water Absorption
|
%
|
ASTM D570
|
1.00
|
成形收缩率
MD(Mold Shrinkage)
|
%
|
ASTM D955
|
1.10
|
成形收缩率
TD(Mold Shrinkage)
|
%
|
ASTM D955
|
1.40
|
伸张断裂强度
Tensile Strength at Break
|
MPa
|
ASTM D638
|
45.00
|
伸张降伏强度
Tensile Strength at Yield
|
MPa
|
|
|
断裂伸张率
Tensile Elongation at Break
|
%
|
ASTM D638
|
100.00
|
伸张弹性系数
Tensile Modulus
|
MPa
|
|
|
弯曲强度
Flexural Strength
|
MPa
|
ASTM D790
|
69.00
|
弯曲弹性系数
Flexural Modulus
|
MPa
|
ASTM D790
|
2000.00
|
艾氏耐冲击强度(缺口式)
Izod Impact Strength (notched)
|
J/m
|
ASTM D256
|
588.00
|
洛式硬度或秀尔硬度
Rockwell/Shore Hardenes
|
|
|
|
热变形温度 0.46 MPa
Heat Distortion Temp
|
℃
|
ASTM D648
|
170.00
|
热变形温度 1.82 MPa
Heat Distortion Temp
|
℃
|
|
|
线膨胀系数10¯5
Coefficient of Linear Thermat Expansion
|
mm/mm/℃
|
ASTM D696
|
9.00
|