牌号
用途级别
Ultrason® P 3010 NAT | BASF | PPSU 物性表
Unreinforced, higher viscosity injection moulding grade, flameretardent and with improved chemical resistance.
Abbreviated designation according to ISO 1043-1: PPSU
流变性能 |
干 / 已调节 |
单位 |
测试标准 |
20 / * |
cm³/10min |
ISO 1133 |
|
360 / * |
°C |
ISO 1133 |
|
10 / * |
kg |
ISO 1133 |
|
0.9 / * |
% |
ISO 294-4, 2577 |
|
1.0 / * |
% |
ISO 294-4, 2577 |
机械性能 |
干 / 已调节 |
单位 |
测试标准 |
- / 2270 |
MPa |
ISO 527-1/-2 |
|
- / 74 |
MPa |
ISO 527-1/-2 |
|
- / 7.8 |
% |
ISO 527-1/-2 |
|
- / N |
kJ/m² |
ISO 179/1eU |
|
- / N |
kJ/m² |
ISO 179/1eU |
|
- / 65 |
kJ/m² |
ISO 179/1eA |
|
- / 24 |
kJ/m² |
ISO 179/1eA |
热性能 |
干 / 已调节 |
单位 |
测试标准 |
220 / * |
°C |
ISO 11357-1/-2 |
|
196 / * |
°C |
ISO 75-1/-2 |
|
212 / * |
°C |
ISO 75-1/-2 |
|
55 / * |
E-6/K |
ISO 11359-1/-2 |
电性能 |
干 / 已调节 |
单位 |
测试标准 |
- / 3.8 |
- |
IEC 60250 |
|
- / 3.7 |
- |
IEC 60250 |
|
- / 17 |
E-4 |
IEC 60250 |
|
- / 89 |
E-4 |
IEC 60250 |
|
- / >1E13 |
Ohm*m |
IEC 60093 |
|
* / >1E15 |
Ohm |
IEC 60093 |
|
- / 44 |
kV/mm |
IEC 60243-1 |
|
- / 150 |
- |
IEC 60112 |
其它性能 |
干 / 已调节 |
单位 |
测试标准 |
1.2 / * |
% |
类似ISO 62 |
|
0.6 / * |
% |
类似ISO 62 |
|
1290 / - |
kg/m³ |
ISO 1183 |
模塑测量的特殊性能 |
干 / 已调节 |
单位 |
测试标准 |
71 / * |
cm³/g |
ISO 307, 1157, 1628 |
试样制备条件 |
价值 |
单位 |
测试标准 |
370 |
°C |
ISO 294 |
|
160 |
°C |
ISO 10724 |
典型数据
加工方法
注塑, 薄膜挤出成型, 异型材挤出成型, 片材挤出成型, 其它挤出成型, 吹塑, 热成型
供货形式
粒料
地区供应
Processing Texts
注塑成型
PREPROCESSING
Pre/Post-processing, max. allowed water content: .02 %
Pre/Post-processing, Pre-drying, Temperature: 140 °C
Pre/Post-processing, Pre-drying, Time: 4 h
PROCESSING
injection molding, Melt temperature, range: 350 - 390 °C
injection molding, Melt temperature, recommended: 370 °C
injection molding, Mold temperature, range: 140 - 180 °C
injection molding, Mold temperature, recommended: 160 °C
Pretreatment
Drying temper ature: 130 - 150°C
Drying time: minimum 4h
recommended dryer: vaccum or dry air dryer
maximum moisture: 0,02 - 0,05%
Ultrason® can be injection molded by any type of machinery on the market, provided that the plasticizing unit and the mold temperature control system have been configured appropriately. The machinery manufacturer must be consulted if any doubts exist on the ability of various parts to withstand the high temperatures required (e.g. barrel, barrel he ad, bolted connections, etc.)
Long residence time in combination with high temperatures should be avoided e.g. by pump out material at regular intervals.
During extended interruptions, the barrel temperature should be lowered to
It has been found out that heating to the requested processing temperature and shutting down or lowering the temperature is best carried out in two steps.
First, the barrel temperatures are set at the lower processing temperat ure range for the particular thermoplastic (340 - 350 °C). As soon as these temperatures have reached a steady state, the material in the barrel is pumped out. Second, the barrel temperature can be set to the required processing temperature or the heaters can be shut down.
原来的高性能非结晶塑料存在接口部位受到冲击应力时容易损坏的缺点。该公司进行的夏氏冲击试验结果表明,ULTRASONE
可承受2000次的高温蒸汽循环,可用高温清洗、杀菌。另外,发生火灾时也不易排放有害物质,因此该公司希望能够在飞机的座套、灯罩、换气阀及行李箱上使用该产品。(
PES |
德国巴斯夫 |
E2010 |
PES |
德国巴斯夫 |
E2010G2 |
PES |
德国巴斯夫 |
E6010 BK |
PES |
德国巴斯夫 |
E6020 |
PES |
德国巴斯夫 |
S3010 |
ASA |
德国巴斯夫 |
757G |
ASA |
德国巴斯夫 |
776S-BK |
ASA |
德国巴斯夫 |
778T |
ASA |
德国巴斯夫 |
778T-BK |
ASA |
德国巴斯夫 |
778T-NC |
ASA |
德国巴斯夫 |
776SE |
ASA |
德国巴斯夫 |
776SE-BK |
ASA |
德国巴斯夫 |
776SE-NC |
ASA |
德国巴斯夫 |
797SUV |
ASA |
德国巴斯夫 |
Q440 |
ASA |
德国巴斯夫 |
757R |
ASA |
德国巴斯夫 |
796M |
ASA |
德国巴斯夫 |
797SE |
ASA |
德国巴斯夫 |
KR2864 |
ASA |
德国巴斯夫 |
KR2864 BK |
ASA |
德国巴斯夫 |
777K |
ASA/PC |
德国巴斯夫 |
2864 |
ASA/PC |
德国巴斯夫 |
2864 BK |
PSU |
德国巴斯夫 |
E2010 |
PSU |
德国巴斯夫 |
S2010 |
PSU |
德国巴斯夫 |
S3010 |
PSU |
德国巴斯夫 |
S2010G6 |
PA6/66 |
德国巴斯夫 |
C40 |
PPSU |
德国巴斯夫 |
P3010 |